PRIMER EP-1020
Two-component, 100 % solids, epoxy resin as a primer
It’s a two-component, 100% solid content, epoxy resin-based. Specially designed as a primer to increase adherence and repair substrates on mortar, concrete or ceramic tiles for flooring and waterproofing systems TECNOFLOOR, TECNOTOP, TECNOCOAT, and DESMOPOL.
Use
Epoxy resin to be used in the following situations in TECNOFLOOR, TECNOTOP, TECNOCOAT and DESMOPOL systems:
- Specially designed to increase the adhesion on concrete, mortar, or ceramic tiles supports.
- Self-leveling application (thick coat)
- Also used as a resin mortar adding SILICA SAND, or calcium carbonate for concrete support preparation
NOTE: call our technical department about the application to other supports or situations
density at 23ºC | 1.05 g/cm³ |
viscosity at 23ºC | 250 cps |
pot life at 23ºC | ± 50 minutes |
drying time at 23ºC | ±60 minutes |
approx. coat consumption | ±150 g/m2 |
mix ratio | 2,20:1 |
GENERAL FEATURES
- High fluidity that allows for a quick and easy application of the product.
- High penetration and sealing on support.
- Excellent adhesion to concrete.
- Epoxy resin 100% solids, Odorless, and solvent-free.
- may yellow on outdoor exposure, due to the action of UV rays, to be an epoxy.
- Do not add water or any solvent.
- Usual coverage per coats: 4-6 m2/kg (±150 to 250 g/m2)
- Applied in several coats, or self-leveling application, the consumption can vary between 200-700 g/m2 (depending on the state of the surface to be treated or existing unevenness)
- The performance, used as a filling mortar is highly variable. Using with SILICA SAND (mix ±1:4), or calcium carbonate (mix ±1:2)
- It can be applied on surfaces with a maximum surface humidity of 4%.
- After 7 days, coming to a cured material total. Preserve the direct contact with water or other reagents until this moment.
- Do not apply at temp. below. 10 ºC or more than 30 ºC, or with relative moisture more than 80%. Do not use hot air guns that burn fossil fuels. These conditions facilitate the appearance of white spots. Use electric heaters.
- The PRIMER EP-1020 should be applied in dry conditions avoiding the presence of humidity or water coming from the surface to be coated or the substrate, whether at the time of application or subsequently (pressure from phreatic water level).
- The component A is red-colored, to mix with the comp. B turns orange. (in the mixed product, doesn’t see this orange color).
PACKAGING
Kit metal tins: 10,3 kg.+4,7kg.
SHELF LIFE
12 months for each product at temperatures between 5° C and 35° C, provided it is stored in a dry place. Once the tin has been opened, the product must be used immediately.
APPLICATION METHODOLOGY
Support
- The concrete slab must be clean, compact, and free of loose particles, grease, oil, cement laitance, curing liquids, or other treatments such as silicones or damaged paintings.
- The surface must be with the pore opened, it is essential to start work with treatment and subsequent shot blasting dust sucked. sanding, therefore, is not recommended rough and open-pored surface ensuring anchoring the primer is sought.
- The concrete has to be more than 28 days old or maximum moisture content of 4%.
- Do not apply PRIMER EP-1020 on concrete with exudations of water or in areas where the inside water may affect the adhesion of the system components.
- Both temperature, environmental and support, should be at least 3 higher than the dew point at the time of the application, so the risk of condensation is reduced.
Mixing
- PRIMER EP-1020 comes in pre-weighed containers suitable for subsequent mixing proportions, partial mixtures is not recommended.
- Pour the contents of Comp. II on Comp. I, and mix with a drill fitted with a stirrer at low speed until achieving a homogeneous product. Special emphasis on shaking the walls and bottom of the container.
- In the case of adding aggregate, make the mixture described above first and, once made, add the aggregate to obtain a homogeneous product.
- Do not add water or any solvents.
APPLICATION METHODS
- Apply PRIMER EP-1020 with the help of a short-haired roller on the support. applying a second layer will be necessary for very absorbent substrates.
- Self-leveling application, using a squeegee or a trowel(thick coat )
- Consumption is 0.200 - 0.400 kg / m² depending on the roughness of the substrate.
- For repair, the concrete surfaces, use this epoxy resin mixed with SILICA SAND (mix ratio ± 1: 4) or calcium carbonate mix ratio(± 1: 2) as a mortar, applied by notched trowel or roller.
- In liquid condition, clean up with DESMOSOLVENT. Once cured, clean up only by mechanical means.
HANDLING
These safety recommendations for handling, are necessary for the implementation process as well as in the pre and post, on exposure to the loading machinery.
- Respiratory Protection: When handling or spraying use an air-purifying respirator.
- Skin protection: Use rubber gloves, remove immediately after contamination. Wear clean body-covering. Wash thoroughly with soap and water after work and before eating, drinking, or smoking.
- Eye / Face: Wear safety goggles to prevent splashing and exposure to particles in the air.
- Waste: Waste generation should be avoided or minimized. Incinerate under controlled conditions in accordance with local laws and national regulations.
Anyway, consult the material and safety data sheet of the product (MSDS) or contact our technical department.
PROPERTIES
PROPERTIES |
VALUE |
Density at 23ºC ISO 1675 |
1.05 g/cm³ |
Viscosity at 23ºC ISO 2555 |
250 cps |
Density comp. A at 23ºC ISO 1675 | 1.25 g/cm³ |
Density comp. B at 23ºC ISO 1675 | 1.10 g/cm³ |
Viscosity comp. A at 23ºC ISO 2555 | 500 - 350 cps |
Viscosity comp. B at 23ºC ISO 2555 | 250 - 450 cps |
Mixing ratio | 2,20:1 |
Solids content ISO 1768 | 100% |
VOC(volatile organic compounds) | 0 g/l comp. A+0 g/l comp. B |
Shore Hardness A DIN 53.505 | >75 |
Adhesion to the concrete |
>2 MPa |
Pot life at 23 ºC |
±50 minutes |
Drying time 23 ºC |
±60 minutes |
Final dry time at 23 ºC |
±2~3 hours |
Recoat range time at 23 ºC |
3~24hours |
Service range temperature |
-20~80 ºC |
Environmental and surface range of temperature for the application |
5~35 ºC |
Max. moisture on the support |
±4 % |
Max. environmental moisture |
±80% |
Dilution |
NEVER |
These values in this table are approximate and can vary depending on the situation of the carrier or application methodology employed